Effect of the addition of silver compounds during the pyrolysis of manganese nitrate on tantalum anodic oxide film

A study of the pyrolysis of an aqueous solution of manganese nitrate in the presence of silver compounds has been carried out. Thermal analysis showed that the MnO₂ formation temperature and the transformation temperature from MnO₂ to Mn₂O₃ shifted towards a lower temperature in the presence of silver acetate. A large particle-size and high crystallinity MnO₂ was formed; this may be a useful method of making an excellent tantalum capacitor with high capacitance.     

掺钛蓝宝石激光晶体中夹杂物的分析

本文用大视场光学显微镜、电子探针观察和分析了掺钛蓝宝石激光晶体中夹杂物的形状、尺寸大小及元素组成，并提出消除和减少这些夹杂物的方法．     

钛容器的特点

根据钛材的化学、物理、力学和工艺性能介绍了钛容器在设计、制造、检验和应用方面的特点。     

Supercritical fluid extraction of daphne (Laurus nobilis L.) seed oil

Laurus nobilis L., commonly known as daphne tree, is an evergreen that belongs to the Lauraceae family. Daphne trees produce grape-sized shiny purplish berries having three parts: flesh, skin, and an inner kernel (single seed). This study examines supercritical CO₂ (SC-CO₂) extraction of oil from daphne seeds. The oil yield of ground seeds varied from 14 to 28% depending on the method and particle size used for oil recovery. Yields were similar for both petroleum ether and SC-CO₂ extraction. The extraction yield decreased significantly with increasing particle size. The amount of extract collected increased exponentially with increasing SC-CO₂ pressure. The highest extraction yield was obtained at the highest temperature studied, 75°C. More than 45% of the oil was lauric acid. SC-CO₂ is a viable technique to obtain high-purity L. nobilis L. seed oil, which is a potential ingredient for the cosmetic industry.     

助催化剂对TiCl_4/MgCl_2催化丙烯高温聚合的影响

研究了助催化剂种类(三甲基铝、三异丁基铝、三正己基铝、三乙基铝和甲基铝氧烷)及其含量对无内、外给电子体的TiCl4/MgCl2催化剂催化丙烯高温(100℃)聚合性能的影响,并用结晶分级分析、示差扫描量热和凝胶渗透色谱等方法分析了所得聚丙烯的结晶熔融行为和微观结构。实验结果表明,聚合温度从70℃升至100℃时,TiCl4/MgCl2催化剂的定向能力基本不变;100℃聚合时,以烷基化能力较弱的三异丁基铝为助催化剂时TiCl4/MgCl2催化剂的活性最高,而采用烷基化能力最强的三甲基铝为助催化剂时TiCl4/MgCl2催化剂的活性最低;100℃聚合时,助催化剂的种类对TiCl4/MgCl2催化剂的定向能力影响很小。     

Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.     

用碳化养护电弧熔炉钢渣制备集料和混凝土

将电弧熔炉(electric arc furnace,EAF)钢渣和石灰混和制成球状集料,置于密闭容器当中,并通入100%的CO2气体进行碳化,在0.506 6MPa保持2h.通过质量法测定添加质量分数为11.94%石灰的EAF钢渣(下同)集料CO2的吸收率为5%,通过红外光谱(infrared,IR)分析测定CO2的吸收率为13.88%.用碳化的钢渣集料制备混凝土再进行碳化养护,同时利用碎石和河砂为集料制备碳化混凝土作为参比样.用质量法测定2种混凝土的碳化率分别为21.14%和10.57%;用IR法的为13.81%和16.97%.碳化后电弧熔炉钢渣集料内生长着大量簇生的犬牙状碳酸钙晶体.     

原位TiCp/Fe复合材料的切削力及切屑形状

从退火态原位TiCp／Fe复合材料的切削力和切屑形状方面分析了其切削性能。研究结果表明其切削力及切削力的波动范围都小于铸态45钢，其切削性能比45钢好。TiCp／Fe复合材料的切屑为C形屑、长紧卷屑和发条状卷屑，在机加工中，产生这几种切屑是比较理想的。从切屑方面看，TiCp／Fe复合材料的切削性能较好。     

复合聚全氟乙丙烯材料的介电及高频击穿性能研究

在聚全氟乙丙烯(FEP)中添加 TiO_2和 Al_2O_3,通过热压成型的方法制备了 FEP/TiO_2复合材料和 FEP/Al_2O_3复合材料,研究了氧化物添加量对复合材料介电常数、介电损耗和高频击穿性能的影响。结果表明,随氧化物含量的增加,复合材料的介电常数和介电损耗均增加;在同一添加量下,TiO_2对复合体系的介电性能影响较大。FEP/TiO_2复合材料的高频击穿性能随 TiO_2含量的增加而下降,在 TiO_2含量为4.0%(质量分数,下同)时,复合材料的损伤阈值已降为 FEP 材料损伤阈值的48.9 %。而 FEP/Al_2O_3复合材料的高频击穿性能随 Al_2O_3含量的增加而升高,当 Al_2O_3含量为1.2%时,复合材料的损伤阈值已增大到 FEP 材料损伤阈值的2倍,达到313 J/m~2。     

用激光粒度分析仪测定二氧化锆粒度

介绍以六偏磷酸钠作为分散剂，采用激光粒度分析仪测量二氧化锆粒度的一种新方法。该方法的测量范围为0．05～300μm。